Use & Application
These consumables are designed for prolonged elevated temperature service up to 600°C. Main areas of application are associated with steam generating power plant, e.g. piping, turbine castings, steam chests, valve bodies and boiler superheaters. Some of the consumables will also find service in refineries where they are used for corrosion resistance to Sulphur bearing crude oil at 250-450°C. Some of the consumables will also find applications in the chemical and petro-chemical industries where they are used for resistance to hydrogen attack in the fabrication of hydrocrackers, coal liquefaction plant and NH3 pressure vessels operating at up to 450°C. In the as-welded condition the consumables also provide a useful source of 300HV hardness weld deposit for build-up or hardsurfacing to resist metal-to-metal wear, heavy impact and the repair of P20 mold steel. Preheat and interpass temperature 250°C minimum, up to 300°C for thick sections. Maintain throughout welding cycle and some time after completion of welding. Apart from some special applications, PWHT will always be required. PWHT temperature is typically 690°C with time being dependent on section thickness.
Alloy type
2¼Cr-1Mo alloyed steel consumables for elevated temperature service.
After PWHT, the microstructure consists of tempered bainite.
Materials to be welded

EN W.Nr.: 11 CrMo 9-10 (1.7383), 10 CrMo 9-10 (1.7380), GS-18CrMo 9 10 (1.7379), GS-12CrMo 9 10 (1.7380), 6CrMo 9 10 (1.7385), 12CrMo 9 10 (1.7375).
ASTM: A387 Gr 21&22, A182 F22, A217 WC9, A234 WP22, A199 T21,T22, A200 T21,T22, A335 P22, A234 WP22.

Products of the line 2Cr1Mo

Product name Material Processes
{{ item.nome }} {{['en-GB'] }} {{ process }} >
Our catalogs

Request informations

Provide your contact information and we'll get back to you with all relevant product specifications and valid freight forwarding solutions.
© Daiko s.r.l 2022 - Viale G. G. Felissent 84/D, 31100 Treviso, Italia
REA 416562 VAT and T.C. IT04907220265 - All rights reserved